STC5680 hardening fluid

Good adhesion to PCTG(tritan) substrate; low rainbow pattern; good abrasion resistance, scratch resistance; excellent chemical resistance.

Product Consulting

18030106835

Intent Message

STC5680 Hardening Fluid Instructions

Product Introduction:

Right.PCTG(tritan) substrate has good adhesion; low rainbow pattern; good abrasion resistance, scratch resistance; excellent chemical resistance.

Advantage Features:

1. Good adhesion to PCTG(tritan) substrate;

2. Lower rainbow pattern;

3. Good wear resistance, scratch resistance;

4. Excellent chemical resistance.

Application areas:

PCTG(tritan) window lenses, sun lenses/optical lenses.

Process Guide:

Special Sex	Typical value
Environmental conditions	20-25°C, 40-60% relative humidity
Environmental cleanliness	1000-10000
Airflow	Filtration, Laminar Flow
Coating temperature	16-18°C
coating filtration	1-5 microns (absolute)
Pull rate	2mm/s
Drying time/Temperature	5-10minutes, infrared/60-70°C
Curing conditions	2hrs@120°C

Data indicators:

1. Solution characteristics:

Characteristics	Test Method	Typical value
Solid content	30min @ 180 ℃	28-30 %
Viscosity (cps）	Rotational viscometer test at 25°C	8-12
Density (g/ml）	Test of the specific gravity meter at 25 ℃	0.950-0.970
Solvent: Water, ethanol, propylene glycol methyl ether

2. Cured coating characteristics:

Characteristics	Test Method	Typical value
Layer thickness (One)	thickness measuring instrument	3-6
Scratch resistance	6-bend lens 0000# steel wool load 200g test 20 back and forth	≦ 5 scars
Attach	the hundred-grid method,3M Tape	100%
Boiled	Boil in 80 ℃ water bath for 30min, 100-meter test	100%

Storage recommendations:

1. It is recommended to store in 2-5 ℃ environment with a shelf life of 3 months;

2. This product contains alcohols, so pay attention to fire prevention during storage and use;

3. This product will react and deteriorate in contact with PVC, silica gel and carbon steel materials. Therefore, please use PTFE, polyethylene, polypropylene, stainless steel materials or containers when using and holding. Do not use PVC, silica gel and carbon steel materials.

Note:

1. This product cannot be mixed with other brands of strengthening liquid. Before using this brand of strengthening liquid, the container should be fully cleaned.,Pipes, filters;

2. In order to ensure that there is no crystal point on the surface, the strengthening solution needs to be filtered with 1um or 2um polypropylene (PP) folded filter element for 12 hours before it can be used for the first time. In the production process, each time the strengthening solution is added, it needs to be added in the auxiliary tank. After addition, it also needs to be continuously circulated and filtered for more than 2 hours before it can be produced again;

3. Before coating, the lens should be cleaned and the room should be clean, and the cleanliness should be between 1000-10000. In the production process, due to the volatilization of the solvent, the viscosity of the strengthening solution will gradually increase, and it can be diluted with isopropanol or ethanol, as long as the solid content is controlled.28-30between%.

Limited Liability (please read carefully):

The Company ensures that the information provided above is accurate. However, because the conditions and methods of using our products are beyond our control, this information is not a substitute for customer testing to ensure that the products are safe, effective and fully satisfactory for a particular end use. We specifically disclaim any other express or implied warranties of fitness or merchantability for a particular purpose and are not responsible for any indirect or incidental damages.